焊接與銀釬焊SOLDERING AND SILVER BRAZING
務必記住所推薦的閥門的用途是什么，并對所應用的環(huán)境進行分析，這樣才能決定選用最適合安裝什么樣的閥門。在安裝正確的閥門之前，為了防止損壞閥門，并保證充分發(fā)揮閥門的工作性能，請閱讀一下安裝指南：Analyze the application to determine which valve is best suited for installations, keeping in mind the service for which the valve is recommended. Before installing the correct valve, review the installation instructions to prevent damage to the valve and to assure its maximum efficiency：
先沿著垂直方向切割管道，并修整、去除毛刺，測量管徑。Cut tube end square. Ream, burr and size.
使用紗布或鋼絲刷清除管道和切割部位，使其金屬表面發(fā)光發(fā)亮。建議不要使用鋼絲絨。Use sand cloth or steel wire brush to clean both ends to a bright metal finish. Steel wool is not recommended.
在管道的外面和焊接罩的內(nèi)部涂上焊劑，焊劑必須完全覆蓋焊接表面。請有節(jié)制地使用焊劑。Apply flux to outside of tube and inside of solder cup. Surfaces to be joined must be completely covered. Use flux sparingly.
要確保閥門處于開啟狀態(tài)。先對管道加熱。盡可能多的將熱從管道傳遞到閥門。避免延長閥門本身的加熱時間。Be sure that valve is fully open. Apply heat to tube first. Transfer as much heat as possible through tube into valve. Avoid prolonged heating of valve itself.
銀釬焊的方法：對需要進行釬焊的部件進行組裝。如果允許涂上焊劑的部件處于直立狀態(tài)，那么焊劑中的水分會蒸發(fā)掉，而干燥的焊劑很容易脫落，致使暴露的金屬表面容易被氧化。在進行連接組裝時，要將管道插入管套直到遇到阻擋為止。組裝是要保證有穩(wěn)固的支撐，使得整個釬焊操作過程中能夠保持在直線位置。Silver Brazing Method: Assemble parts to be brazed. If fluxed parts are allowed to stand, the water in the flux will evaporate, and dried flux is liable to flake off, exposing metal surfaces to oxidation. Assemble joint by inserting tube into socket hard against the stop. The assembly should be firmly supported so that it will remain in alignment during the brazing operation.
注：對于1英寸或更大公稱通徑的閥門，一次性將連接部件加熱到所需溫度比較困難。為了在整個大面積上保持正常的溫度，通常情況下需要兩個焊槍。建議對整個管套區(qū)域進行適當?shù)念A熱。建議采用乙炔火焰對連接部件進行加熱。首先從離閥門1英寸的地方開始對管道進行加熱，然后圍繞著管道短距離上下交替對管道進行火焰烘烤，并以適當?shù)慕嵌刃D(zhuǎn)管道，避免燒穿管道�；鹧嬉B續(xù)運動，不允許停留在某一點上。NOTE: On one-inch and larger valves, it is difficult to bring the whole joint up to temperature at one time. It will frequently be found desirable to use a double-tip torch to maintain the proper temperature over the larger area. A mild pre-heating of the whole socket area is recommended. Apply heat to parts to be joined. The preferred method is by oxy-acetylene flame. Heat tube first, beginning one inch from edge of valve. Sweep flame around tube in short strokes up and down at right angles to run of tube. To avoid burning through tube, the flame should be in continuous motion and not allowed to remain on any one point.
在閥門的套筒底座用火焰進行烘烤。加熱要均勻，用火焰對閥門及管道進行火焰烘烤的過程要延續(xù)到閥門上的焊劑不再發(fā)出聲音。不要對閥門過度加熱。Apply flame to valve at base of socket. Heat uniformly, sweeping flame from valve to tube until flux on valve becomes quiet. Avoid excessive heating of valve.
當焊劑變成液態(tài)并且在管道和閥門上呈現(xiàn)半透明狀態(tài)時，開始將火焰沿著連接部件的軸線進行進退烘烤，以保持連接部件、特別是閥門套筒底座部位的熱度。When flux appears liquid and transparent on both tube and valve, start sweeping flame back and forth along axis of joint to maintain heat on parts to be joined, especially toward base of valve socket.
使用適量的焊料：如果使用線狀焊料，那么對公稱通徑為3/4英寸的閥門就要采用3/4英寸的焊料，等等。如果使用的焊料太多，那么有些焊料可能會流過管道阻擋部位，并堵塞密封區(qū)域。在安裝連接部件時，可以看到焊料和釬焊合金繼續(xù)流動Use just enough solder: with wire solder, use 3/4" for a 3/4" valve, etc. If too much solder is used, it may flow past tube stop and clog sealing area. When joint is filled, a continuous run of solder or brazing alloy will be visible.
銀釬焊法：將焊線或焊桿點在閥門里的管道套座上。當焊桿或焊線進入連接處時要將火焰從其上面移開。當合金流進連接處時，要前后移動火焰。達到適當?shù)臏囟群�，合金將迅速容易地流進管道外殼和閥門套管之間的空間。連接處被充滿后，就會看到焊接合金的邊緣。Silver Brazing Method: Apply brazing wire or rod at point where tube enters valve socket. Keep flame away from rod or wire as it is fed into the joint. Move flame back and forth as alloy is drawn into joint. When the proper temperature is reached alloy will flow readily into space between tube outer wall and valve socket. When joint is filled, a continuous rim of brazing alloy will be visible.